| Physical Properties |
Metric |
English |
Comments |
| Density |
1.20 g/cc |
0.0434 lb/in3 |
|
| Linear Mold Shrinkage |
0.00500 - 0.00700 cm/cm |
0.00500 - 0.00700 in/in |
1/16" thick plaque |
| Linear Mold Shrinkage, Transverse |
0.00600 - 0.00700 cm/cm |
0.00600 - 0.00700 in/in |
1/16" thick plaque |
| Melt Flow |
29.0 g/10 min |
29.0 g/10 min |
224°C/1.2 kg load |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore A |
90.0 - 98.0 |
90.0 - 98.0 |
ASTM D2240 |
| Hardness, Shore D |
54.0 - 62.0 |
54.0 - 62.0 |
ASTM D2240 |
| Tensile Strength at Break |
42.0 MPa |
6090 psi |
Tensile stress at break. |
| Elongation at Break |
540 % |
540 % |
|
| 50% Modulus |
0.00841 GPa |
1.22 ksi |
|
| 100% Modulus |
0.0103 GPa |
1.49 ksi |
|
| 300% Modulus |
0.0207 GPa |
3.00 ksi |
|
| Flexural Modulus |
0.0758 GPa |
11.0 ksi |
|
| Tear Strength |
131 kN/m |
747 pli |
|
| Taber Abrasion, mg/1000 Cycles |
10.0 |
10.0 |
H22 Wheel |
| Compression Set |
30.0 % |
30.0 % |
23°C. |
| Compression Set, Elevated Temperature |
40.0 % |
40.0 % |
70°C |
| Tensile Set |
60.0 % |
60.0 % |
Elongation set after break |
| |
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear 20°C |
151 μm/m-°C |
83.9 μin/in-°F |
|
| Vicat Softening Point |
89.0 °C |
192 °F |
|
| Glass Temperature |
-24.0 °C |
-11.2 °F |
|
| Clash Berg Stiffness Temperature |
-39.0 °C |
-38.2 °F |
|
| |
| Processing Properties |
Metric |
English |
Comments |
| Processing Temperature |
193 - 210 °C |
379 - 410 °F |
Optimum Extrusion Temperature |
| Melt Temperature |
213 - 216 °C |
415 - 421 °F |
产品关键词：TPU
|
|
|
| |
| 姓 名： |
叶飞 (女士) |
| 职 务： |
|
| 电 话： |
0571-88162717 |
| 移动电话： |
13575753257 |
| 传 真： |
0571-88162617 |
| 地 址： |
中国浙江省杭州市潮王路古河巷27号红石中央花苑麒麟阁1栋1单元1801室 |
| 邮 编： |
310005 |
| 企 业： |
杭州奥圆工贸有限公司 |
|
 |
|
|
|
橡塑
<< 热塑性弹性体
回到页首 